Download Lotader® reactive terpolymers brochures and technical data sheets.

The data displayed in the tables below are typical values but should not be considered as commercial specifications.

Lotader® MAH Grades

Grades Technical data sheet Butyl acrylate content (%Wt) Maleic anhydride content (%Wt) Melt Index (g/10min) Melting point (°C) Vicat point (°C) Tensil strengh at break (MPa) Elongation at break (%) Hardness shore D
3210 6 3.1 5 107 76 12 600 46
3410 17 3.1 5 89 47 8 700 32
4210 6.5 3.6 10 105 69 10 650 46
    Methyl acrylate content
             
3430 15 3.1 7 84 45 12 750

30

4503   20 0.3 8 80 45 9 750

25

4513T 24 0.3 8 96 42 - -

-

4613   24 0.3 7 98 - - -

-

    Ethyl acrylate content
             
 4700   29 1.3  7 65 <40 5 800  
 5500   20 2.8  20 80 45 10 700 93*
 6200   6.5 2.8 40 102 66 6 600 36
 8200   6.5  2.8  200 100 57 6 400 26
HX8290   17 2.8 70 85 <40 6 700  
LX4110    5  3  5 105 78 11 650 46
TX8030    13  2.8  3 95 65 12 700 36

*Hardness Shore A

MFI: 190°C, 2.16kg

Lotader® GMA grades

Grades

Technical data sheet

Glycidyl methacrylate content (%Wt) Butyl acrylate content (%Wt) Melt Index (g/10min) Melting point (°C) Vicat point (°C) Tensil strengh at break (MPa) Elongation at break (%) Hardness shore A/D
AX8700   8 25 9 71 <40 4 860 81/25
AX8750   5 25 12 74 <40 5 840 84/26

 

Grades

Technical data sheet

Glycidyl methacrylate content (%Wt) Vinyl acetate content (%Wt) Melt Index (g/10min) Melting point (°C) Vicat point (°C) Tensil strengh at break (MPa) Elongation at break (%) Hardness shore A/D
AX8670T*   9 15 10 85-90 - - - -

*In development

Grades

Technical data sheet

Glycidyl methacrylate content (%Wt) Methyl acrylate content (%Wt) Melt Index (g/10min) Melting point (°C) Vicat point (°C) Tensil strengh at break (MPa) Elongation at break (%) Hardness shore D
AX8820   4.5 0 2 107 88 - - -
AX8840   8 0 5 104 87 8 400 50
AX8900   8 24 6 65 <40 4 1100 18
AX8930   3 25 7 (65) <40 - - -

MFI: 190°C, 2.16kg